- Steel Rebars[10]
- Metal Coating Machinery[10]
- Steel Wire[6]
- Metal Building Materials[2]
- Other Metal Processing Machinery[10]
- Cleaning Equipment[10]
- Spray Booths[10]
- Steel Pipes[7]
- Fencing[10]
- Stainless Steel Balls[10]
- Woodworking Machinery Parts[6]
- Conveyors[3]
- Hydraulic Parts[1]
- Engine Parts[1]
- Alternative Energy Generators[1]
- Dust Collector[1]
- Machinery Parts Processing Services[1]
- Other Machinery[2]
- Contact Person : Mr. Sales LuHuan
- Company Name : Wuxi Luhuan Cleaning Machine Co., Ltd.
- Tel : 86-510-85607793
- Fax : 86-510-85607717
- Address : Jiangsu,Wuxi,Xin'an Industrial Zone, New Economic Development Zone, Wuxi City, Jiangsu Province. China
- Country/Region : China
- Zip : 214135
Cast Steel Shot (VENO-S230)
Product Introduction(ISO9001)
LuHuan cast steel shot is professionally manufactured by Wuxi LuHuan Co., Ltd in china mainland.
Size: S70,S110,S170,S230,S280,S330,S390,S460,S550,S660,S780
Diameter: 0.2mm,0.3mm,0.5mm,0.6mm,0.8mm,1.0mm,1.2mm,1.4mm,1.7mm,2.0mm,2.5mm Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Usage Surface cleaning and rust removing for cast iron, cast steel, steel plates and steel pipes, especially used in shot blasting machine and penning machine.
Main Chemistry
Chemistry
(C) 0.70-1.20%
(Mn) 0.35-1.20%
(Si) 0.40-1.20%
(S) N0.05%
(P) N0.05%
Average Hardness 40-50HRC(377-509HV)
Deviation ±3.0HRC(±40HV)
Minumum Density 7.2g/cm3
1) LuHuan Cast Steel Shot 2) For shot blasting / peening machine 3) High quality 4) Long durability 5) High strength
Product Introduction(ISO9001)
LuHuan cast steel shot is professionally manufactured by Wuxi LuHuan Co., Ltd in china mainland.
Size: S70,S110,S170,S230,S280,S330,S390,S460,S550,S660,S780
Diameter: 0.2mm,0.3mm,0.5mm,0.6mm,0.8mm,1.0mm,1.2mm,1.4mm,1.7mm,2.0mm,2.5mm Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Usage Surface cleaning and rust removing for cast iron, cast steel, steel plates and steel pipes, especially used in shot blasting machine and penning machine.
Main Chemistry
Chemistry
(C) 0.70-1.20%
(Mn) 0.35-1.20%
(Si) 0.40-1.20%
(S) N0.05%
(P) N0.05%
Average Hardness 40-50HRC(377-509HV)
Deviation ±3.0HRC(±40HV)
Minumum Density 7.2g/cm3
Cast Steel Shot (VENO-S230)